Retort pouch and coextruded film therefor

ABSTRACT

A seal layer for use in large institutional-sized retort pouches comprises an ABA film structure wherein the A layers are each composed of a blend of a minor amount of an elastomer and a major amount of a polyolefin, and the B layer is composed of a blend of a major amount of an elastomer and a minor amount of a polyolefin. Retort pouches made with this ABA film structure as the seal layer exhibits improved impact strength.

BACKGROUND OF THE INVENTION

This invention relates generally to retort pouches. In one aspect it relates to a coextruded three layer film for use in retort pouches wherein each layer contains elastomer. In another aspect, the invention relates to a three layer laminate, one of which is a coextruded three ply film, for use in retortable pouches. In still another aspect the invention relates to a method of packaging food for retorting.

DESCRIPTION OF THE PRIOR ART

There is a trend in the food packaging industry to replace metal cans with plastic containers, notably pouches containing sterilized or pre-cooked foods. Such retort pouches offer many advantages over rigid metal packages: faster cook/sterilizing time, less shelf storage space, easier disposal, improved food taste, etc. The pouches are typically three layer laminations of an outer film (e.g., biax oriented nylon and/or polyester), a middle moisture and oxygen barrier film (e.g., aluminum foil, PVDC, or EVOH), and an inner heat seal layer film (PP, PPRC, or LLDPE or blends thereof). Adhesives to join the three layers together are typically of the polyurethane and/or maleated polyolefin types. (The resin abbreviations used herein are defined in "Description of Preferred Embodiments".)

Large No. 10 cans (those containing about 3.2 liters of liquid food) have been slow to convert to flexible retort pouches. Large plastic containers used to package foods have been limited to high acid foods (e.g., catsup) which do not require sterilization to kill botulism toxin. In such containers, LLDPE is often selected as the inner heat seal layer film because of its low cost, toughness and drop impact resistance. However, LLDPE cannot be used in large institutional-size retort pouches (volumetric content larger than 1 liter) which require sterilization, because it softens at typical high temperature sterilization or retort temperatures (121° C. and higher). Although PP or PPRC films can be and are used in smaller size retort pouches (in the order of 0.25 to 1 liter content) because of their higher temperature resistance, they are unacceptable in the larger size pouches because they do not possess adequate toughness or drop impact strength to prevent breakage. With small containers, hydraulic forces resulting from vertical impact are not large. However, with large containers, the hydraulic forces become excessive, particularly on lateral seals. Because of this deficiency there exists a definite market need for institutional size pouches (greater than 1 liter and preferably 2 liter and larger) possessing a tough inner ply heat seal film which is resistant to high temperature retorting temperatures.

Blending elastomer into PP and PPRC is one well established method for improving film toughness and is being practiced commercially. PPRC monolayer film modified with PIB is used as the inner seal layer of medical enteral pouches used to deliver nutritional fluid to hospital patients unable to take food orally. These small 3-layer laminated pouches are typically one liter in size and weigh approximately 2.2 lbs. At least one side of these pouches consists of an all-plastic construction so that the fluid level can be monitored. In order to assure adequate impact toughness, these pouches are subjected to vertical drop tests. Typical vertical drop heights for these products are 4-6 feet. For greater drop height performance, smaller pouches (in the order of 0.5 liters) are sometimes used. However, pouches of this type are far too small for use as institutional food pouches.

European Patent Application No. 0,165,791 discloses a composite film structure comprising rubber-containing core and polyolefin resin. The skin layers of this composite however, contain no rubber. As demonstrated below, rubber (elastomer) in both the skin and core layers improves performance of the pouch.

SUMMARY OF THE INVENTION

It has been discovered that by utilizing a special coextruded inner heat seal layer in a retortable pouch, the problem of room temperature impact strength of large containers is effectively overcome. Although retortable pouches are available in a variety of sizes and constructions, those used in food packaging almost all include a barrier layer and an inner seal layer. The inner seal layer of the retortable pouch of the present invention comprises a coextruded multilayer film which may be an ABA or an ABC structure, where A is the inner skin layer, C the outer layer, and B the core layer. As used herein, the inner layer A is the layer of the package in contact with with the food and the outer layer C is adjacent to the barrier layer (with or without adhesives).

The A and B layers comprise a blend of an elastomer and a polyolefin, preferably PP, more preferably PPRC. Outer skin layer C may be any polyolefin suitable for interfacing with the barrier resin/foil, but preferably has the same composition as A, making the seal layer an ABA structure. Layers A and B each include sufficient elastomer to increase impact strength to he final structure. However, skin layer A contains substantially less elastomer than core layer B. The amount of elastomer in the total film should be in excess of 50 wt% but not more than 70 wt% and preferably not more than 60 wt%. The amount of elastomer in skin layer(s) A should be sufficiently small to avoid or minimize blocking or sticking on the film roll but sufficiently large to add to the impact strength of the 3 layer structure. ABA/ABC thickness ratios may vary within wide limits but preferably range from about 3:94:3 to 20:60:20.

The present invention also includes a pouch structure per se, comprising an outer structural layer; a barrier layer and the three ply inner seal layer of the structure described above. The three ply ABA or ABC structures are useful in retortable pouches which exhibit exceptionally high impact strength and are particularly suitable for use in large institutional-sized retortable flexible containers (larger than 1 liter e.g., 1.25 liters and preferably between 1.5 and 4.0 liters and most preferably between 1.8 and 3.5 liters large).

DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross section view of a laminated film constructed according to the present invention.

FIG. 2 is a pouch made from the film of FIG. 1.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

In its broadest embodiment, the invention comprises a multilayer film which is particularly useful in retort pouches. In many institutions such as hospitals, military, and schools, large retort pouches have potential application. A retort pouch must possess the following properties, all of which are provided or affected by the inner seal layers:

1. they must be heat sealable for closing the container securely following filling;

2. they must be flexible and yet have sufficient toughness and impact strength to enable the pouch to withstand severe abuse testing in accordance with industry shipping standards.

3. they must be capable of withstanding sterilization at temperatures in the range of 121° C.-135° C. to kill botulism;

4. they must possess non-blocking properties in that the interior opposed faces of the container must not stick together which would impede filling of the pouch;

5. the film used in the pouches must be processable without sticking as it is unrolled from the film roll during manufacture of the pouches and subsequent sterilization;

6. they must have sufficient capacity to be economical. (Institutions serving large numbers of people are not likely to use extensively containers having capacities less than one liter.)

Although retortable pouches, one panel of which is represented as 10 in FIG. 1, are available in various constructions, they generally include the following layers: an outer structural layer 11, a barrier layer 12, and a seal layer 13 laminated together with suitable adhesive tie layers. The retort pouch layers are described separately below.

Structural Layer: The structural layer 11 provides structural strength, abrasive resistance and a printable surface for the pouch. It normally is composed of a thermoplastic such as polyolefins, polypropylene [e.g., propylene homo polymers (PP) and copolymers], polyester, nylon, and the like. Biaxially oriented nylon and biaxially oriented polyester are the preferred structural layers. Although not essential to the pouch, the structural layer is preferred since as noted above it adds strength, durability, and printability to the pouch.

Barrier Layer: The barrier layer 12 is substantially impermeable to oxygen for protecting the food medium contained in the pouch. Barrier layer materials include aluminum foil, thermoplastic films such as ethylene vinyl alcohol (EVOH), polyvinylidenedichloride (PVDC), polyvinyl alcohol (PVA), and the like. Aluminum foil is the preferred barrier layer. In packaging where oxygen barrier requirements are not stringent, biaxially oriented nylon or polyester are sometimes employed. The compositions and methods of manufacture of barrier layers and structural layers are well known in the industry and are described in the published literature.

Seal Layer: The main function of the seal layer 13 is to provide a substance which is heat sealable (fusible) with itself to seal the pouch.

An important aspect of the present invention is the composition of the seal layer which enables the pouch to satisfy the six requirements mentioned above. The present invention contemplates the use of a coextruded film as the seal layer, comprising an ABA composite or an ABC composite wherein A is the inner layer of the film, B is a core layer, and C is the outer layer of the film.

The inner layer (A) [and preferably the outer layer (C)] and the core layer (B) each comprises two essential ingredients: a polyolefin and an olefinic elastomer which are blended in different ratios. The core layer is elastomer rich--more than 50 wt% elastomer--and the inner layer (and preferably the outer layer) is elastomer lean--less than 50wt% elastomer.

The polyolefin resins which are suitable for use in the practice of this invention for blending with the elastomer are those which have a semi-crystalline or crystalline melting point of at least 110° C. Illustrative, non-limiting examples of the polyolefins suitable for use in the practice of this invention are polypropylene (PP), linear low density polyethylene (LLDPE) (e.g., a copolymer of ethylene and 3-15% of an olefin having 4 to 12 carbon atoms) and polybutylene (PB). As used in the specification and claims, the term "polypropylene" includes homopolymers of propylene as well as reactor copolymers of propylene (PPRC) which include both random copolymers and impact copolymers. Random copolymers contain about 1 to about 6 wt% ethylene or an alpha olefin monomer of 4 to 16 carbon atoms, and impact copolymers contain from 6 to 20 wt% ethylene or alpha olefin comonomer of 4 to 16 carbon atoms. The polypropylene can be highly crystalline isotactic or syndiotactic polypropylene. The density of the PP or PPRC ranges from about 0.89 to about 0.91 g/cc and the MFR is typically in the range of 0.5 to 5.0. Blends of these polyolefin resins may be used. For example, LLDPE may be blended into PP, not at a high enough concentration to harm thermal stability, but at a concentration to favorably affect heat sealability. The propylene content of the inner layer A should be at least 20 wt%.

As demonstrated by the experiments described below, PPRC (specifically random copolymer) gave the best results in improvements in the impact strength and accordingly is preferred for blending with the elastomer resins.

The rubbers (elastomeric resins) which can be used in the practice of this invention include both synthetic and natural rubbers; preferably the rubbers have a glass transition temperature (Tg) of less than 0° C. Illustrative, non-limiting examples of rubbers suitable for use in the practice of this invention include polyisobutylene (PIB), butyl rubber, halogenated butyl rubber, ethylene propylene rubber (EPM), ethylene-propylenediene rubber (EPDM), polyisoprene, polychloroprene, styrene-butadiene rubber, polybutene copolymers, nitrile rubbers, chlorosulfonated polyethylene, etc. While polyisobutylene (PIB) is not a true rubber because it cannot be vulcanized, it can be utilized in the practice of this invention provided that the PIB has a viscosity average molecular weight (Flory) of about 900,000 to about 1.6 million.

The term "rubber" as used in the specification and claims means any natural or synthetic polymer which can be vulcanized or cured so as to exhibit elastomeric properties. For the purpose of this invention, PIB is considered a rubber although it cannot be vulcanized.

The terms EPM and EPDM are used in the sense of their ASTM designations (ASTMD-1418-72a). EPM is an ethylene-propylene copolymer which can be cross-linked by radiation curing or peroxide curing.

As used in the specification and claims the term "EPDM" means terpolymers of ethylene and alphaolefin and non-conjugated diene. The non-conjugated diolefin can be straight chain, branched chain or cyclic hydrocarbon di-olefins having about 6 to about 15 carbon atoms such as:

A. straight chain dienes such as 1,4-hexadiene and 1,6-octadiene;

B. branched chain acyclic dienes such as 5-methyl-1,4-hexadiene; 3,7-dimethyl1-1,6-octadiene; 3,7-dimethyl1-1,7-octadiene and the mixed isomers of dihydro-myricene and dihydroocinene;

C. single ring alicyclic dienes such as 1,3-cyclopentadiene; 1,4-cyclohexadiene; 1,5-cyclo-octadiene and 1,5-cyclododecadiene;

D. multi-ring alicyclic fused and bridged ring dienes such as tetrahydroindene, methyl, dicyclopentadiene; bicyclo(2,2,1)-hepta-2,5-diene; alkenyl, alkylidene, cycloalkenyl and cycloalkylidene norbornenes such as 5-methylene-2-norbornene (MNB), 5-propenyl-2-norbornene, 5-isopropylidene-2-norbornene, 5-(4-cyclopentenyl)-2-norbornene, 5-cyclohexylidene-2-norbornene, 5-vinyl-norbornene and norbornadiene.

Of the non-conjugated dienes typically used to prepare EPDM terpolymers the preferred dienes are dicyclopentadiene, 1-,4-hexadiene, 5-methyl-2-norbornene and 5-ethylidene-2-norbornene. Particularly preferred diolefins are 5-ethylidene-2-norbornene (ENB) and 1,4-hexadiene.

EPDM elastomers and their general method of manufacture are well known in the art. The preferred EPDM elastomers contain about 20 to about 90 wt% ethylene, more preferably about 30 to 80 wt% ethylene, most preferably about 35 to about 75 wt% ethylene.

The alpha-olefins suitable for use in the preparation of EPDM are preferably C₃ -C₁₆ alpha olefins. Illustrative non-limiting examples of such alpha olefins are propylene, 1-butene, 1-pentene, 1-hexane, 1-octene and 1-dodecene. The alpha olefin is generally incorporated into the EPDM polymer at about 10 to about 80 wt%, more preferably at about 20 to about 70 wt%. The non-conjugated diene is incorporated into the EPDM at about 0.5 to about 15 wt%; more preferably about 1 to about 5 wt%, e.g., 3 wt%.

The term "nitrile rubber" means an acrylonitrile copolymer rubber. Suitable nitrile rubbers comprise rubbery polymers of 1,3-butadiene and about 20-50 wt% acrylonitrile. Any nitrile rubber which is a "solid" rubber having an average molecular weight of at least 50,000 and preferably between about 100,000-1,000,000 can be used. Commercially available nitrile rubbers suitable for the practice of the invention are described in Rubber World Blue Book, 1980 Edition, "Materials and Compounding Ingredients for Rubber," pages 386-406, which is incorporated herein by reference.

Butyl rubber is a copolymer of an isoolefin and a conjugated multiolefin. The useful copolymers comprise a major portion of isoolefin and a minor amount, preferably not more than 30 wt%, of a conjugated multiolefin. The preferred copolymers comprise about 85-99.5 wt% (preferably 95-99.5 wt%) of a C₄ -C₇ isoolefin, such as isobutylene, and about 15-0.5 wt% (preferably about 5-0.5 wt%) of a multiolefin of about 4-14 carbon atoms. These copolymers are referred to in the patents and literature as "butyl rubber"; see, for example, the textbook Synthetic Rubber by G. S. Whitby (1954 edition by John Wiley and Sons, Inc.), pages 608-609, etc. which is incorporated herein by reference. The term "butyl rubber" as used in the specification and claims includes the aforementioned copolymers of an isoolefin having 4-7 carbon atoms and about 0.5 to 20 wt% of a conjugated multiolefin of about 4-10 carbon atoms. Preferably these copolymers contain about 0.5 to about 5% conjugated multiolefin. The preferred isoolefin is isobutylene. Suitable conjugated multiolefins include isoprene, butadiene, dimethyl butadiene, piperylene, etc.

Commercial butyl rubber is a copolymer of isobutylene and minor amounts of isoprene. It is generally prepared in a slurry process using methyl chloride as a vehicle and a Friedel-Crafts catalyst as the polymerization initiator. The methyl chloride offers the advantage that AlCl₃, a relatively inexpensive Friedel-Crafts catalyst is soluble in it, as are the isobutylene and isoprene comonomers. Additionally, the butyl rubber polymer is insoluble in the methyl chloride and precipitates out of solution as fine particles. The polymerization is generally carried out at temperatures of about -90° C. to -100° C. See U.S. Pat. Nos. 2,356,128 and 2,356,129 incorporated herein by reference.

In the halogenation process, butyl rubber in solution is contacted with chlorine or bromine in a series of high-intensity mixing stages. Hydrochloric or hydrobromic acid is generated during the halogenation step and must be neutralized. For a detailed description of the halogenation process see U.S. Pat. Nos. 3,029,191 and 2,940,960, as well as U.S. Pat. No. 3,099,644 which describes a continuous chlorination process, all of which patents are incorporated herein by reference.

The rubbers used in the practice of this invention are preferably utilized in their unvulcanized state. The preferred rubber is PIB.

The core layer (B) and skin layers (A and C) of film composite 13 preferably have the following construction:

    ______________________________________                                                  Composition (wt %)                                                                             Thickness                                                      Elastomer                                                                               Polyolefin (% of Total)                                      ______________________________________                                         Outer Layer (C)                                                                             0-40      60-100    3-20                                          Core Layer (B)                                                                            >50-75      25-<50    60-94                                         Inner Layer (A)                                                                            10-40     60-90      3-20                                          Total Composite                                                                           >50-70     <30-50     2-10 mils                                     Preferred Construction                                                         Outer Layer (C)                                                                            15-30     70-85      7-15                                          Core Layer (B)                                                                            >55-70     30-45      70-86                                         Inner Layer (A)                                                                            15-30     70-85      7-15                                          Total Composite                                                                           >50-60      40-<50    4-7 mils                                      ______________________________________                                    

As indicated above the total elastomer content of the composite seal layer 13 comprises more than 50% in order to impart the necessary impact strength to the pouch. The polyolefin, particularly PPRC, provides for shrinkage stability of the film and retortability without sacrificing impact strength. The elastomer in the inner layer A contributes to impact strength and heat seal strength; excessive elastomer therein is undesirable since it results in roll sticking and/or container blocking. The gradient approach (i.e., rubber lean skin and rubber rich core) yields the highest total rubber content without film blocking.

The compositions of this invention may also include rubber extender oils as well as processing aids and stabilizers, fillers and the like.

Food pouches are generally steam autoclaved at about 121° C. in order to sterilize the food. The pouches prepared with the use of composite film as the seal layer 13 according to this invention must not only withstand the autoclave conditions, they must also exhibit a low water loss both during autoclaving and in storage. Rubbers based on isobutylene, e.g., PIB and butyl rubber, have the lowest water vapor transmission rate among rubbers, and also are broadly FDA regulated. Hence, they are the preferred rubbers for use in this invention.

Preparation of compositions for each layer usable in this invention can be achieved in several different ways. The components may be brought into intimate contact by, for example, dry blending these materials and then passing the overall composition through a compounding extruder. Alternatively, the components may be fed directly to a mixing device such as a compounding extruder, high shear continuous mixer, two roll mill or an internal mixer such as a Banbury mixer. The optional ingredients previously described can be added to the composition during this mixing operation. It is also possible to achieve melt mixing in an extruder section of a coextrusion apparatus. Overall, the objective is to obtain a uniform dispersion of all ingredients and this is readily achieved by inducing sufficient shear and heat to cause the plastics component(s) to melt. However, time and temperature of mixing should be controlled as is normally done by one skilled in the art so as to avoid molecular weight degradation.

Although ABC structures may be employed for fabrication by coextrusion, as mentioned previously, it is preferred to use an ABA film. This film may be coextruded by using conventional extruding and casting equipment wherein one extruder casts the core layer (B) and another extruder casts the skin layer (A). Chill rolls and silicon rolls also may be employed in the casting process. The three layer coex film may be prepared and stored as a roll for fabrication into the pouch film in subsequent operations.

RETORT POUCH

As mentioned previously, the composite film forms the inner seal layer of a retort pouch 10A having the following structure:

    ______________________________________                                                      THICKNESS                                                                               Broad          Preferred                                        COMPO-         Range          Range                                            SITION  mils   % of Total                                                                               mils % of Total                                ______________________________________                                         Structural                                                                              thermo-          0-25         5-20                                    Layer    plastic                                                               Barrier Layer                                                                           barrier          3-15         4-10                                             resin/foil                                                            Seal Layer                                                                              composite 2-10   60-97   4-7  70-90                                            film                                                                  ______________________________________                                    

As shown in FIG. 2, the pouch 10A preferably is made by laminating the three layers 11, 12, and 13 forming a roll stock having the cross section of FIG. 1. The roll stock then is used to form two panels 14 and 15, cutting the panels to the proper size, and heat sealing three of the four sides of the aligned edges 16, 17 and 18 of the panels, leaving one side open 19 to permit filling with food or other perishable goods.

The three layers may be laminated together using conventional equipment and techniques.

Suitable adhesives, or tie layers, may be used to adhere the component layers together. For example, adhesives such as heat curable polyurethane are useful at the interface of nylon layer 11 and aluminum foil layer 12 and at the interface of aluminum layer 12 and the seal layer 13. Likewise, maleic-grafted polyolefins may be used at the interface of nylon layer 11 and PVDC or EVOH 12, and at the interface of the ABA (or ABC) seal layer 13 of the present invention. Other tie resins are well known in the art.

The laminated roll stock is processed into pouches using conventional equipment and techniques. The form, fill and seal (F/F/S) machinery process is one such technique. In this process, two superimposed layers of the laminated film of the desired width with interfacing seal layers are fed into the packaging machine. Bar seals fuse three sides of the square or rectangular pouch and a jaw separates the pouch with one open end. Food is then introduced into the pouch through the open end. Finally, the machine heat seals the open end producing a fully closed pouch.

For large institutional containers, the panels for pouches will be sufficiently large to provide the pouch with a capacity ranging from greater than 1 (e.g., about 1.2 liters) to 5 liters, preferably between 1.5 to 4.0 liters, and most preferably between 1.8 and 3.5 liters. These pouches are adapted to be filled with a liquid or semiliquid food (e.g., low acid particulates such as stew). Packaging machines which fill by the F/F/S process include Prodo Pak's Model HFF-1000 and N & W Packaging System Model MAX 2014.

Preformed pouches may also be employed in this operation, pouches with an open end are prepared and subsequently filled with the liquid or semiliquid substance in a separate step.

The packaged food is then sterilized at temperatures of 121° C. to 135° C. for 3 to 60 minutes depending on the type of food and food processing techniques.

One of the problems associated with institutional-sized plastic containers for packaging liquid or semi-liquid food is their inability to withstand impact forces following heat sterilization. The heat weakens the seals and the hydraulic forces on dropping creates high stresses in the horizontal direction. Thus, an essential property of each pouch is that it is capable of withstanding impacts during handling and transport. The industry has developed a number of tests for determining the suitability of the pouches for shipping in cases; two of which are ASTM and NSTA standards described below. In addition, it has been found that drop tests on individual pouches provides a reliable test for determining (qualitatively) the impact strength of pouches. These tests involve multiple drops of each pouch before retorting. The term "multiple drop tests" means that the pouch is dropped on each of the four sealed edges and on one flat surface from an elevation of 10 feet onto a flat metal surface.

EXPERIMENTS

Effects of Rubber on Heat Sealability of PP:

Tests are carried out on the heat seal strength of monolayer film of various blends of PP and EPDM (Vistalon® 3708 marketed by Exxon Chemical Company). These tests indicated that the addition of the elastomer up to about 40 wt% improves heat seal strength for elastomer/PP blend film. Elastomer content about 40% in the film showed little or no improvement in heat seal strength. Retorting a blend of 40% elastomer and 60% PP at 121° C. for 30 minutes reduced seal strength by only 19%; the remaining seal strength was adequate for packaging purposes.

Pouch Tests:

Pouches (12 inch×12 inch and 10 inch×13 inch) were made using a 4-mil or 7-mil seal layers having the following compositions:

                  TABLE 1                                                          ______________________________________                                         SEAL LAYER FILM X                                                                                                Thickness                                    Layer  Composition       wt %     (% of Total)                                 ______________________________________                                         A      VISTANEX L-100.sup.1 /PPRC.sup.2                                                                 24/76    10                                           B      VISTANEX L-100.sup.1 /PPRC.sup.2                                                                 65/35    80                                           C      VISTANEX L-100.sup.1 /PPRC.sup.2                                                                 24/76    10                                           ______________________________________                                          .sup.1 PIB, EXXON Chemical Co.                                                 .sup.2 3 wt % ethylene, 1 MFR                                            

The seal film was laminated with structural and barrier layers to form two roll stocks which were used to fabricate pouches having the compositions of Pouches 1 and 2 described in Table 2. The Pouch 2 structures made from one of the roll stocks were 12"×12" and were fabricated, filled, and sealed using Prodo Pak's Model HFF1000 Filler/sealer. The seal temperatures were about 410° F. with a horizontal dwell of 4 seconds and a vertical dwell of three-fourths second and a line speed of 12 pouches per minute. Seal pressures were 80 psi for horizontal seals and 70 psi for vertical seals. Pouch 1 structures made from the other roll stock were 10"×13" and were made using preformed equipment at approximately the same process conditions.

                  TABLE 2                                                          ______________________________________                                         LAMINATED POUCHES                                                                           Pouch 1    Pouch 2                                                ______________________________________                                         Structural Layer:                                                                             PET/T.sub.3  BN/T.sub.3                                         Barrier Layer: Al/T.sub.4   Al/T.sub.4                                         Seal Layer:    Seal Layer X Seal Layer X                                       ______________________________________                                          BN -- Biax nylon (60 gauge)                                                    Al -- Aluminum Foil (35 gauge)                                                 T.sub.3  Tie layer marketed by Morton Chemical as Adcote 550.                  T.sub.4  Tie layer marketed by Morton Chemical as Adcote 50640/9L10.           PET  Biaxially oriented polyester manufactured by DuPont (48 gauge).     

The pouches were filled with 1.9 liters or 3.18 liters of liquid, and drop tested by the multiple drop test method before retorting. The following summarizes the test results:

                  TABLE 3                                                          ______________________________________                                         MULTIPLE DROP TESTS                                                                      Pouch 1 (1.9 Liters)                                                                       Pouch 2 (3.18 Liter)                                     ______________________________________                                         No. Samples Tested                                                                         50 (4 mil)    75 (4 mil)                                           (Thickness of Seal        50 (7 mil)                                           Layer)                                                                         Results     Passed multiple                                                                              Passed multiple                                                  drop test     drop test                                            ______________________________________                                    

The above tests demonstrate that (a) the retorted pouches made in accordance with the present invention exhibit improved impact strength and (b) the improved results are due to the composition of the seal layer.

In order to assure safe handling of the pouches packed in shipping containers during transit, the pouches (after filling and retorting) should pass tests established by the ASTM and/or the NSTA. Such test include Vibration Testing for Shipping Containers (ASTM D999-75) and Drop Testing for Shipping Containers (ASTM D775-61), and NSTA Test Procedures, Project IA. The pouches of the present invention packed in shipping containers (2 stacks, 3 high) are capable of passing the ASTM tests and the more stringent NSTA tests. This capability of the institution sized packages, particularly those between 1.8 and 3.5 liters has not been achieved with prior art pouches.

The following Container Drop Tests on Pouches 1 and 2 demonstrate this capability and exemplify the high impact strength of the pouches.

Pouches had the structures and compositions of Pouches 1 and 2 described in Table 2 and were retorted for about 60 minutes at about 121° C. Corrugated cardboard cases were packed with six of each type of pouch after retorting. Each case was provided with two vertical compartments which snugly contained three stacked pouches. Each case was tested by the ASTM or NSTA Drop Tests described above (including vibration tests prior to dropping). TABLE 4 summarizes the Container Drop Tests.

                                      TABLE 4                                      __________________________________________________________________________     CONTAINER DROP TESTS                                                               Seal Layer Liquid                                                                              No. Con-                                                   Pouch                                                                              Thickness                                                                            size Contents                                                                            tainers                                                                             Test       Test                                       Type                                                                               Mils  inches                                                                              liters                                                                              Tested                                                                              Method     Results                                    __________________________________________________________________________     1   4     10 × 13                                                                       about 1.9                                                                           20   ASTM D775-61 (12")                                                                        Passed                                     2   4     12 × 12                                                                       about 3.18                                                                          10   ASTM D775-61 (12")                                                                        Passed                                                              and NSTA                                              2   7     12 × 12                                                                       about 3.18                                                                          10   ASTM D775-61                                                                              Passed                                                              and NSTA                                              1   7     10 × 13                                                                       about 1.9                                                                            5   ASTM D775-61 (12)                                                                         Passed                                     __________________________________________________________________________

As indicated above the Multiple Drop Tests are carried out before retorting and the Container Drop Tests are carried out after retorting. Tests have shown that pouches that pass the Multiple Drop Tests also pass the ASTM and NSTA Container Drop Tests. The Multiple Drop Test thus provides a reliable, simple and inexpensive test for determining the quality of shipping pouches.

Blocking Tests:

Tests using a roll of monolayer seal layer film containing 65 wt% VISTANEX and 35 wt% PPRC exhibited severe blocking, demonstrating the problem associated with high rubber content. The roll stock used in preparing Pouches 1 and 2, however, exhibited little or no blocking. 

We claim:
 1. Multilayer heat sealable and retortable film comprising:(a) an inner layer comprising a blend of a major weight portion of a polyolefin and a minor weight portion of an elastomer, said inner layer being heat sealable with itself; (b) a core layer comprising a blend of a major weight portion of an elastomer and a minor weight portion of a polyolefin resin; and (c) an outer layer comprising a polyolefin; the total elastomer content in the layers being more than 50 wt% thereof.
 2. The multilayer film of claim 1 wherein the polyolefin in the core layer and inner layer is a propylene polymer.
 3. The multilayer film of claim 2 wherein propylene polymer is PPRC.
 4. The multilayer film of claim 1 wherein the elastomer is PIB.
 5. The multilayer film of claim 1 wherein the said outer layer comprises from 0 to 40 wt% of an elastomer and from 60 to 100 wt% of a polyolefin; the core layer comprises more than 50 wt% and not more than 75 wt% of said elastomer; and the inner layer comprises from 10 to 40 wt% of said elastomer.
 6. The multilayer film of claim 5 wherein said inner layer comprises from 15 to 30 wt% of said elastomer and said core layer comprises from 55 to 70 wt% of said elastomer.
 7. The multilayer film of claim 6 wherein the elastomer in the layers is PIB and the polyolefin in the layers is PPRC.
 8. A coextruded multilayer film comprising an ABC layer construction wherein:(a) the A layer is the inner layer and comprises a blend of a propylene polymer and from 10 to 40 wt% of an elastomer, said A layer being heat sealable with itself; (b) the B layer is the core layer comprising from more than 50 to 75 wt% of an elastomer and from 25 to less than 50 wt% of a propylene polymer; (c) the C layer is the outer layer comprising a propylene polymer and from 0 to 40 wt% of an elastomer, the ratio of the thickness of ABC layers being from 3:94:3 to 20:60:20; and (d) the total elastomer content of layers A, B, and C is more than 50 wt% but not more than 70 wt%.
 9. The film of claim 8 wherein the elastomer in the ABC layers is the same and is PIB and the propylene polymer in the ABC layers is the same and is PPRC.
 10. The film of claim 9 wherein the C layer is the same composition as A layer.
 11. The film of claim 10 wherein the elastomer concentration in layer B comprises from 55 to 70 wt% of the blend and the concentration of the elastomer in layers A and C comprise from 15 to 30 wt% thereof.
 12. The film of claim 11 wherein the total elastomer content of the film is greater than 50 and not more than 60 wt%.
 13. The multilayer film of claim 9 wherein the PPRC is a propylene impact copolymer containing from 6 to 20 wt% of ethylene.
 14. A film laminate comprising:(a) the coextruded film of claim 8; and (b) a barrier layer of a film or foil laminated to the C layer of said coextruded film.
 15. The laminate of claim 14 wherein the barrier layer is aluminum foil and wherein the laminate further comprises a structural layer laminated to the barrier layer.
 16. A retortable pouch comprising first and second film panels, each panel comprising:(a) a barrier layer; and (b) an inner heat seal coextruded multilayer of claim 8;said film panels having aligned edge portions heat fused together thereby defining a container having a volume capacity of more than 1 liter and not more than 5 liters.
 17. The pouch of claim 16 wherein the panels each include a structural layer laminated to the barrier layer and are of sufficient area to provide the container with a capacity of between 1.5 and 4.0 liters of liquid or semiliquids, and the pouch is capable of withstanding multiple drop tests when filled with a liquid or semiliquid before retorting.
 18. The pouch of claim 17 wherein the pouch has a capacity of between 1.8 and 3.5 liters and, with other substantially identical pouches, is capable of withstanding case drop tests as defined in ASTM D775-61, after retorting at a temperature of at least 121° C.
 19. The pouch of claim 17 wherein the barrier layer is composed of aluminum foil and the structural layer is composed of biaxially oriented nylon or polyester.
 20. A retortable, heat sealed pouch comprising:(a) first and second panels, each comprising:(i) a structural film which comprises not more than 20% of the panel thickness; (ii) an oxygen barrier of aluminum foil and comprising not more than 20% of the panel thickness laminated to the structural film; (iii) a coextruded multilayer film having the composition of claim 8 and being 2 to 10 mils thick wherein the C layer is laminated to the barrier film or foil; (b) said panels having their edge portions heat sealed thereby defining an enclosed container having a capacity in excess of 1 liter; (c) a liquid or semiliquid substance contained in said enclosed container, said pouch being capable of withstanding case drop tests in accordance with NSTA Test procedures after retorting at a temperature of at least 121° C.
 21. The pouch of claim 20 wherein the structural layer is biaxially oriented nylon and the pouch has a capacity of between 1.8 and 3.5 liters.
 22. A coextruded multilayer film useful in retortable pouches which comprises:(a) an inner seal layer comprising a blend of from 70 to 85 wt% of a propylene random copolymer and 15 to 30 wt % of PIB, said inner seal layer being heat fusible with itself; (b) a core layer comprising a blend of from 30 to 45 wt% of a propylene random copolymer and from 55 to 70 wt % of PIB; (c) an outer layer comprising a blend of from 70 to 85 wt% of a propylene random copolymer and from 15 to 30 wt% of PIB; (d) wherein the thickness ratio of the three layers ranges from 3:94:3 to 20:60:20 and the elastomer content of the three layers constitutes more than 50 but not more than 60 wt%.
 23. A method of packaging liquid or semiliquid food comprising:(a) forming substantially identical panels, each comprising an outer structural layer composed of a thermoplastic resin, a core layer of a barrier film or foil, and an inner seal layer of coextruded multilayer film comprising an ABC layer construction wherein:(i) the A layer is the inner layer and comprises a blend of a propylene polymer and from 10 to 40 wt% of an elastomer, said A layer being heat sealable with itself; (ii) the B layer is the core layer comprising from more than 50 to 75 wt% of an elastomer and from 25 to less than 50 wt% of a propylene polymer; (iii) the C layer is the outer layer comprising a propylene polymer and from 0 to 40 wt% of an elastomer, the ratio of the thickness of ABC layers being from 3:94:3 to 20:60:20; and (iv) the total elastomer content of layers A, B, and C is more than 50 wt% but not more than 70 wt%; (b) superimposing one panel over the other panel with interfacing inner seal layers; (c) heat sealing all but one edge of the aligned edges of the panels forming an interior pouch having separable internal panel portions and an opening at on edge portion; (d) filling the interior of the panels through said opening with more than 1 liter of a perishable liquid or semiliquid food; (e) heat sealing said opening thereby enclosing said food; (f) retoring said filled pouch at a temperature about 121° C. to kill botulism toxin in the food and; (g) packaging the pouch in a case.
 24. A method as defined in claim 23 wherein the pouch is substantially square or rectangular in shape and the area of each panel is sufficient to provide the pouch with a capacity of between 1.8 and 3.5 liters.
 25. The method of claim 23 wherein said case is drop tested in accordance with ASTMD775-61.
 26. The multilayer film of claim 9 wherein the PPRC is a random copolymer containing about 1 to 6 weight percent ethylene.
 27. The multilayer film of claim 26 wherein the random copolymer contains about 3 weight percent ethylene. 